Name

-

corundum

Superior H-AL

1 st grade H-Al

2 nd ,3 rd grade

clay

Al-Mg mortar

Magnesia-Al mortar

Spinel mortar

Al-C mortar

Zircon mortar

Mullite sillimanite mortar

Light weight clay mortar

GPA-90

TA-85

A-75

LQ-53(55)

NQ-42

AM-70

MA-42

MA-30

AC-60

GZ-50

Al2O3   %

≥

90

85

75

55   53

42

50

42

70

50

( ZrO2)50

56

40

MgO      %

≥

-

-

-

-

-

30

43

8

C:6

-

-

-

Refractoriness ℃

≥

1790

1790

1790

1770

1710

1790

1790

1790

1790

1790

1790

1650

Setting time,min

1 ～ 3

1 ～ 3

1 ～ 3

1 ～ 3

1 ～ 3

1 ～ 3

1 ～ 3

1 ～ 3

2 ～ 5

1 ～ 3

1 ～ 3

1 ～ 3

MPa adhensive strength

110 ℃ ,24h

≥

2

2

1.0

1.0

1.0

1.0

1.5

1.0

0.7

1.0

1.0

0.8

1500 ℃ ,2h

≥

8

6

6

-

-

-

-

-

-

-

-

-

1400 ℃ ,2h

≥

-

-

-

4

-

5

-

-

-

-

-

-

1400 ℃ ,3h

≥

-

-

-

-

-

-

-

6

-

3.0

3.0

-

1200 ℃ ,2h

≥

-

-

-

-

-

-

-

-

-

-

-

1.0

1200 ℃ ,3h

≥

-

-

-

-

3.0

-

-

-

-

-

-

-

Grain size

≤ 0.5mm

≥

97

97

97

97

97

-

-

-

-

-

-

-

≤ 0.074mm

≥

50

50

50

50

50

-

-

-

60

50

60

50

0.5 ～ 1mm

≤

-

-

-

-

-

-

-

-

12

-

-

-

＞ 1mm

-

Not permit to exist

APPLICATIONS

 The products is used for  refractories .

PACKING

 in 25kg /bag then 40bags  into 1mt big bag or 880bags into container

STORAGE  AND SHELF LIFE

  At least 18 months in dry conditions

AVAILABILITY

 100-1000 metric tons per month

SHIPMENT

 60 days after L/C date

Brand

F-YZK-GY

F-YZK-GL-P

F-YZK-GL-S

F-YZK-NT

Al2O3        %

≥ 90

≥ 60

≥ 42

LC           %

1450 ℃ ,3h

1400 ℃ ,3h

1400 ℃ ,3h

1350 ℃ ,3h

± 0.5

± 1.0

± 1.0

± 1.0

CCS        MPa

≥ 60

≥ 20

≥ 30

≥ 20

BD       g/ cm3

≥ 2.7

≥ 2.4

≥ 2.4

≥ 2.3

APPLICATIONS

The products is used for  refractories .

PACKING

in 25kg /bag then 40bags  into 1mt big bag or 880bags into container

STORAGE  AND SHELF LIFE

At least 18 months in dry conditions

AVAILABILITY

100-1000 metric tons per month

SHIPMENT

 60 days after L/C date

Brand

-

F-JL-1

F-JL-2

F-DL-1

F-DL-2

Al2O3         %

≥

65

50

45

45

SiC            %

≥

8

30

10

20

F · C           %

≥

3

4

-

-

BD g/ cm3

110 ℃ ,2h

≥

2.70

2.55

-

-

1450 ℃ ,2h

≥

2.60

2.50

2.0

2.35

CCS MPa

110 ℃ ,2h

≥

5.0

6.0

-

-

1450 ℃ ,2h

≥

15.0

10.0

-

-

MOR MPa

110 ℃ ,2h

≥

2.5

2.0

2.0

2.0

1450 ℃ ,2h

≥

4.5

4.0

-

-

LC          %

-

( 1450 ℃ ,2h) ± 0.5

( 1450 ℃ ,2h) ± 0.5

APPLICATIONS

The products is used for  refractories .

PACKING

in 25kg /bag then 40bags  into 1mt big bag or 880bags into container

STORAGE  AND SHELF LIFE

At least 18 months in dry conditions

AVAILABILITY

100-1000 metric tons per month

SHIPMENT

 60 days after L/C date

Brand

-

F-JA-90

F-JA-80

F-JA-70

F-JA-65

F-JA-55

Al2O3       %

≥

90

80

70

65

55

Refractoriness   ℃

≥

1790

1790

1730

1710

1710

BD        g/ cm3

≥

2.85

2.75

2.65

2.35

2.2

LC %

1500 ℃ × 3h

-

± 0.5

± 1.0

± 1.0

-

-

1450 ℃ × 3h

-

-

-

-

± 1.0

-

1400 ℃ × 3h

-

-

-

-

-

± 1.0

CCS MPa

110 ℃ × 24h

≥

70

50

45

40

30

1500 ℃ × 3h

≥

80

60

50

-

-

1450 ℃ × 3h

≥

-

-

-

50

-

1400 ℃ × 3h

≥

-

-

-

-

40

MOR MPa

110 ℃ × 24h

≥

5.0

4.0

4.0

4.0

3.0

1500 ℃ × 3h

≥

8.0

4.0

5.0

-

-

1450 ℃ × 3h

≥

-

-

-

4.0

-

1400 ℃ × 3h

≥

-

-

-

-

3.5

MST        ℃

-

1600

1600

1500

1500

1400

APPLICATIONS

The products is used for  refractories .

PACKING

in 25kg /bag then 40bags  into 1mt big bag or 880bags into container

STORAGE  AND SHELF LIFE

At least 18 months in dry conditions

AVAILABILITY

100-1000 metric tons per month

SHIPMENT

 60 days after L/C date

Brand

-

F-PM-0.5

F-PM-0.8

F-PM-1.0

F-PM-1.5

Al2O3       %

≥

23

33

27

55

SiO2         %

≥

45

23

54

-

BD        g/ cm3

-

0.5 ± 0.05

0.8 ± 0.05

1.0 ± 0.05

1.5 ± 0.05

LC   %

1000 ℃ ,3h

-

± 0.6

± 0.8

± 0.3

-

1250 ℃ ,3h

-

-

-

-

± 1.0

CCS   MPa

Normal temperature

≥

1.0

3.0

4.0

10

1000 ℃ ,3h

≥

0.8

2.5

3.0

-

1250 ℃ ,3h

≥

-

-

-

8.0

MOR   MPa

Normal temperature

≥

0.3

1.0

1.2

3.0

1000 ℃ ,3h

≥

0.2

0.8

1.0

-

1250 ℃ ,3h

≥

-

-

-

2.0

TCR    W/m · k

250 ℃ ≤

0.17

0.2

0.26

0.34

500 ℃ ≤

0.20

0.23

0.3

0.38

APPLICATIONS

 The products is used for  refractories .

PACKING

 in 25kg /bag then 40bags  into 1mt big bag or 880bags into container

STORAGE  AND SHELF LIFE

  At least 18 months in dry conditions

AVAILABILITY

 100-1000 metric tons per month

SHIPMENT

 60 days after L/C date

Brand

F-XQJ

0.6

0.8

1.0

Al2O3      %

＞ 25

＞ 28

＞ 30

( 110 ℃ )BD   g/ cm3

0.6 ± 0.1

0.8 ± 0.1

1.0 ± 0.1

( 700 ℃ )TCR   W/m · k

＜ 0.22

＜ 0.25

＜ 0.30

ST       ℃

600

800

900

Max.service temperature

800

1000

1200

Service part

Insulating   layer   of   roof

APPLICATIONS

 The products is used for  refractories .

PACKING

 in 25kg /bag then 40bags  into 1mt big bag or 880bags into container

STORAGE  AND SHELF LIFE

  At least 18 months in dry conditions

AVAILABILITY

 100-1000 metric tons per month

SHIPMENT

 60 days after L/C date

Name

Coating for tundish

Gunning mix

Material

MGT

Magnesia calcium

MP

magnesia

LTP

Alumina carborundum

Al2O3       %

-

-

≥ 75

MgO        %

≥ 65

≥ 78

-

CaO        %

≥ 15.0

-

SiC ≥ 8

BD       g/ cm3

≥ 2.2

≥ 2.4

≥ 2.3

LC         %

( 1500 ℃ ,3h)0 ～－ 2.5

-

-

CCS       MPa

( 110 ℃ ,24h) ≥ 10

-

-

( 1500 ℃ ,3h) ≥ 6

-

-

( 1400 ℃ ,3h) ≥ 8

( 1500 ℃ ,3h) ≥ 20

( 1500 ℃ ,3h) ≥ 15

APPLICATIONS

 The products is used for  refractories .

PACKING

 in 25kg /bag then 40bags  into 1mt big bag or 880bags into container

STORAGE  AND SHELF LIFE

  At least 18 months in dry conditions

AVAILABILITY

 100-1000 metric tons per month

SHIPMENT

 60 days after L/C date

Brand

Common alkaline resistance

High strength alkaline resistance

High-alumina castable

High alumina high strength castable

Corundum castable

F-GT-40

F-GT-48

F-A-75

F-H-80

F-G-90

Al2O3      %

≥

40

48

75

80

90

SiO2       %

≤

50

40

20

15

6

BD         g/ cm3

2.1-2.3

2.2-2.4

≥ 2.7

≥ 2.8

≥ 3.0

MOR MPa ≥

110 ℃ after drying

5

8

8

10

11.5

1100 ℃ after heating

3

8

5

10

11.5

1500 ℃ after heating

-

-

-

-

11.5

CCS MPa ≥

110 ℃ after drying

50

70

80

80

100

1100 ℃ after heating

30

70

50

80

100

1500 ℃ after heating

-

-

-

-

100

LC   %

1100 ℃

± 0.5

± 0.5

± 0.3

± 0.3

± 0.3

1500 ℃

-

-

-

-

± 0.3

Service temperature ℃

1200

1300

1400

1500

1700

Water          %

8-10

5-6

8-10

6-8

5-6

Installation method

Vibrating

Main application

1-4 grade preheater and related pipes

5 grade preheater,ascension flue of decomposing furnace,secondary air pipe,chain zone

Kiln entrance of front and back,hoods of kiln door,parts front of cooler and of   high temp. abrasion resistance part

Same as A-75,but high temperature resistance and strength is better

Front entrance of dry process cement kiln,burner of third wind pipe

APPLICATIONS

The products is used for  refractories .

PACKING

in 25kg /bag then 40bags  into 1mt big bag or 880bags into container

STORAGE  AND SHELF LIFE

At least 18 months in dry conditions

AVAILABILITY

100-1000 metric tons per month

SHIPMENT

 60 days after L/C date